PENENTUAN PARAMETER PROSES TERHADAP KUAT TEKAN MATERIAL BONE GRAFT HIDROKSIAPATIT (HA) – GLISERIN DENGAN RESPONSE SURFACE METHODOLOGY (RSM)

Ahsan, Taufiq Nur (2022) PENENTUAN PARAMETER PROSES TERHADAP KUAT TEKAN MATERIAL BONE GRAFT HIDROKSIAPATIT (HA) – GLISERIN DENGAN RESPONSE SURFACE METHODOLOGY (RSM). Other thesis, UPN 'Veteran" Yogyakarta.

	Text 5. Daftar Isi_122180048_Taufiq Nur Ahsan.pdf Download (179kB)
	Text 6. Daftar Pustaka_122180048_Taufiq Nur Ahsan.pdf Download (105kB)
	Text 1. Skripsi Fulltext_122180048_Taufiq Nur Ahsan.pdf Restricted to Repository staff only Download (12MB)
	Text 2. Cover_122180048_Taufiq Nur Ahsan.pdf Download (75kB)
	Text 4. Lembar Pengesahan_122180048_Taufiq Nur Ahsan.pdf Download (329kB)
	Text 3. Abstrak_122180048_Taufiq Nur Ahsan.pdf Download (35kB)

Abstract

xii
ABSTRAK
Kebutuhan akan bone graft saat ini semakin meningkat dikarenakan
bertambahnya penyakit cacat tulang. . Pada tahun 2019, insidensi (kasus baru) patah
tulang di seluruh dunia yaitu sebanyak 178 juta kasus, dimana angka tersebut mengalami
peningkatan sebesar 33,4% dibandingkan dengan tahun 1990. Prevalensi kasus patah
tulang yang diakibatkan oleh kejadian akut seperti jatuh atau kecelakaan lalu lintas
maupun sebagai komplikasi dari suatu penyakit, seperti osteoeporosis di seluruh dunia
terdapat 455 juta kasus, dimana angka tersebut meningkat 70% dari tahun 1990,
sedangkan di Daerah Istimewa Yogyakarta menunjukkan dalam kurun waktu 2019
sampai 2020 terdapat 1.249 kejadian patah tulang.
Pada penelitian ini akan dilakukan pembuatan bone graft yang berasal dari
campuran Hidroksiapatit dengan Gliserin dengan metode freeze drying. Bone graft
kemudian dilakukan uji kuat tekan dan uji SEM-EDX yang kemudian dilakukan
pengolahan data dengan menggunakan Response Surface Methodology (RSM)
Diperoleh nilai kuat tekan tertinggi 1,262 MPa dan terendah 0,080 MPa.
Berdasarkan Response Surface Methodology (RSM) dengan bantuan Software Minitab
diperoleh apabila untuk mendapat respon optimal tersebut diperlukan HA : Gliserin 35 :
65, waktu pengadukan campuran 5 jam, serta waktu proses freeze drying selama 6 jam
dengan predicted value kuat tekan sebesar 0,9267 MPa. Dengan adanya hasil dari uji
SEM dapat diketahui jika rendahnya atau belum mencapai target uji kuat tekan
dikarenakan ukuran pori yang cukup besar yang menyebabkan bone graft menjadi rapuh.
Kemudian dari hasil SEM EDX diperoleh bahwa kandungan yang terdapat pada bone
graft di dominasi oleh kalsium oksida, difosfor oksida, dan karbon.
Kata kunci: Bone graft, hidroksiapatit, gliserin, uji kuat tekan, response surface
methodology (RSM)
xiii
ABSTRACT
The need for bone graft is currently increasing due to the increase in bone
defects. . In 2019, the incidence (new cases) of fractures worldwide was 178 million
cases, which is an increase of 33.4% compared to 1990. The prevalence of fracture cases
caused by acute events such as falls or traffic accidents or as a complication of a disease,
such as osteoeporosis worldwide there are 455 million cases, which is an increase of
70% from 1990, while in the Special Region of Yogyakarta shows that in the period from
2019 to 2020 there were 1,249 cases of fractures.
In this study, bone graft will be made from a mixture of hydroxyapatite with
Glycerin with the freeze drying method. Bone graft was then tested for compressive
strength and SEM-EDX test which was then carried out data processing using response
surface methodology (RSM)
Obtained the highest compressive strength value of 1.262 MPa and the lowest of
0.080 MPa. Based on the Response Surface Methodology (RSM) with the help of Minitab
Software, it is obtained if to get the optimal response, HA: Glycerin 35: 65, mixed stirring
time is 5 hours, and freeze drying process time is 6 hours with an predicted compressive
strength value of 0.9267 MPa. With the results of the SEM test, it can be known if the low
or has not reached the pressure strength test target due to the large enough pore size that
causes the bone graft to become brittle. Then from the results of SEM EDX, it was
obtained that the content contained in the bone graft was dominated by calcium oxide,
phosphorus oxide, and carbon.
Keywords: Bone graft, hydroxyapatite, glycerin, compressive strength test, response
surface methodology (RSM)

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Bone graft, hydroxyapatite, glycerin, compressive strength test, response surface methodology (RSM)
Subjects:	H Social Sciences > HD Industries. Land use. Labor
Divisions:	Faculty of Engineering, Science and Mathematics > School of Engineering Sciences
Depositing User:	Eko Yuli
Date Deposited:	04 Oct 2022 08:42
Last Modified:	04 Oct 2022 08:42
URI:	http://eprints.upnyk.ac.id/id/eprint/31279

Actions (login required)

View Item