PT. Tansri Madjid Energi merupakan perusahaan tambang bijih emas yang berlokasi di Desa Lebong, Kecamatan Lebong Utara, Kabupaten Lebong, Provinsi Bengkulu. Perusahaan masih terus mengembangkan alternatif pengolahan yang akan diterapkan dengan melakukan penelitian. Salah satunya adalah tes Gravity Recoverable Gold (GRG) yang akan diketahui derajat liberasi emas, mineralogi, peningkatan kadar dan perolehan emas menggunakan alat Knelson Concentrator. Parameter tersebut akan digunakan untuk menganalisis proses pengolahan yang diterapkan khususnya dengan metode konsentrasi gravitasi. Oleh karena itu perlu dilakukan analisis pada hasil uji laboratorium yang telah dilakukan oleh pihak perusahaan. Pengamatan optik mengungkapkan bahwa emas terliberasi dalam konsentrat pada ukuran butir ≤ 80μm dengan sebagian besar emas tersebut dalam keadaan terliberasi sempurna dan emas dalam electrum juga hadir dengan mayoritas emas native. Selain itu pada sampel yang diuji terindikasikan bahwa kuarsa merupakan penyusun utama dalam batuan dikuti feldspar serta mineral sulfida seperti pyrite, chalcopyrite, sphalerite, covellite, digenite, marcasite dan oksida besi seperti hematite dalam jumlah yang sangat kecil. Kemudian hasil pengujian yang telah dilakukan juga mendapatkan nilai calculated grade sebesar 2,27 ppm dan head grade sebesar 2,3 ppm. Berdasarkan hasil perhitungan yang telah dilakukan didapatkan beberapa hasil. Pertama, bahwa semua nilai Kriteria Konsentrasi (KK) > 2,5 yang berarti pemisahan secara konsentrasi gravitasi dapat dilakukan pada berbagai ukuran. Kedua, didapatkan nilai perolehan total sebesar 64,59%. Ketiga, didapatkan nilai nisbah konsentrasi total sebesar 1,76. Keempat, berdasarkan hasil analisis pertimbangan dari aspek perolehan, peningkatan kadar dan nisbah konsentrasinya dipilihlah ukuran fraksi 75μm sebagai ukuran umpan untuk Knelson Concentrator. Hal ini dikarenakan pada ukuran fraksi 75μm baik perolehan pada tahap 1 dan 2 (65,30% dan 66,80%), peningkatan kadar konsentrat pada tahap 1 dan 2 (7,36 dan 2,43) serta nisbah konsentrasinya pada tahap 1 dan 2 (2,68 dan 2,71) didapatkan hasil yang tinggi. PT. Tansri Madjid Energy is a Mining Company of gold ore that located on Lebong Village, North Lebong Subdistrict, Lebong Regency, Bengkulu Province. The Company is still developing an alternate process will be applied with some research. One of them is Gravity Recoverable Gold (GRG) test will known the gold liberation, mineralogy, the increased of grade and the gold recovery using Knelson Concentrator. Those parameter will be used to analyze applied unit operation especially with gravity concentration method. For that reason, analysis in laboratory test result by company is need to be done. Optic monitoring reveals that liberated gold in size of grain ≤ 80μm concentrate with most of the gold liberated perfectly and gold in electrum also present with the most of gold is native. Beside in the tested sample there’s indication that quartz is the main constituent in the rocks that followed by feldspar and sulfide mineral like pyrite, chalcopyrite, sphalerite, covellite, digenite, marcasite, and iron oxide like hematite in lesser amount. Then the test result also gain total calculated grade of 2,27 ppm and head grade of 2,3 ppm. Based on the calculation, there are some result. First, all values of concentration criteria > 2,5 that means separation in a gravity concentration could be done in various size. Second, value of total recovery 64,59% was obtained. Third, total ratio of concentration 1,76 was obtained as well. Fourth, based on the analysis from gold recovery aspect, the increased grade and its ratio of concentration, the size fraction of 75μm as feed size for Knelson Concentrator was choosen. This is because at the size fraction of 75μm, either at result stage 1 and 2 (65,30% and 66,80%), the increased of concentrate grade at stage 1 and 2 (7,36 and 2,43) along with the ratio of concentration at stage 1 and 2 (2,68 and 2,71), a high result was obtained.
| Item Type: | Thesis (Other) |
|---|---|
| Subjects: | T Technology > TN Mining engineering. Metallurgy |
| Divisions: | Faculty of Engineering, Science and Mathematics > School of Engineering Sciences |
| Depositing User: | Eko Suprapti |
| Date Deposited: | 23 May 2016 06:56 |
| Last Modified: | 23 May 2016 06:56 |
| URI: | http://eprints.upnyk.ac.id/id/eprint/2138 |
Actions (login required)
 |
View Item |