PENGARUH VARIASI ARUS DAN WAKTU PENCELUPAN PROSES ELEKTROPLATING HARD CHROME TERHADAP KETEBALAN DAN KEKERASAN PADA BAJA JIS G 3131 SPHC

SANTOSO, BISMOYO ENGGAR (2022) PENGARUH VARIASI ARUS DAN WAKTU PENCELUPAN PROSES ELEKTROPLATING HARD CHROME TERHADAP KETEBALAN DAN KEKERASAN PADA BAJA JIS G 3131 SPHC. Other thesis, UPN 'Veteran" Yogyakarta.

	Text ABSTRAK.PDF Download (70kB)
	Text COVER.PDF Download (77kB)
	Text DAFTAR_PUSTAKA.PDF Download (8kB)
	Text PENGESAHAN.PDF Download (79kB)
	Text SKRIPSI_BISMOYO_ENGGAR_S_11.PDF Restricted to Repository staff only Download (749kB)
	Text DAFTAR_ISI.PDF Download (91kB)
	Text DAFTAR_ISI.PDF Download (91kB)

Abstract

v
ABSTRAK
Elektroplating hard chrome merupakan proses pelapisan logam menggunakan
ion kromat (CrO3) yang diendapkan secara langsung pada logam dasar, dengan
memanfaatkan sifat-sifat krom yaitu sifat tahan panas, korosi, erosi, dan koefisien
gesek rendah.Penelitian ini bertujuan untuk mengetahui pengaruh perbedaan kuat
arus dan waktu pencelupan terhadap ketebalan dan kekerasan. Spesimen yang
digunakan baja JIS G 3131 SPHC berukuran 50x40 mm dengan ketebalan 2 mm.
Proses coating dilakukan pada suhu dan jarak yang sama yaitu 30oC dan 10 cm.
Parameter yang digunakan arus sebesar 2, 3, 4 A dan waktu 40, 50, 60 menit.
Pengujian yang dilakukan yaitu pengukuran ketebalan dan kekerasan mikrovickers.
Ketebalan lapisan tertinggi terjadi pada spesimen dengan kuat arus 3 A dan waktu 50
menit sebesar 2,522 µm. Sedangkan nilai terendah terjadi pada spesimen dengan kuat
arus 2A dan waktu 40 menit sebesar 1,6 µm. Kemudian nilai kekerasan mikro
tertinggi sebesar 420,498 VHN,terjadi pada spesimen dengan kuat arus 3A dan waktu
50 menit. Sedangkan nilai terendah sebesar 213,088 VHN, terjadi pada spesimen
dengan kuat arus 2A dan waktu 40 menit.
Kata Kunci : Coating, Elektroplating Hard Chrome, Arus, Waktu, Ketebalan,
Kekerasan, Baja, JIS G 3131 SPHC.
vi
ABSTRACT
Electroplating hard chrome is a metal plating process using chromate ions
(CrO3) that are deposited directly on the base metal, by utilizing chrome properties,
namely heat resistance, corrosion, erosion, and low friction coefficient. This study
aims to determine the effect of differences in current strength and dyeing time on
thickness and hardness. The specimen used jis G 3131 SPHC steel is 50x40 mm in
size with a thickness of 2 mm. The coating process is carried out at the same
temperature and distance, namely 30oC and 10 cm. The parameters used currents
amount to 2, 3, 4 A and time 40, 50, 60 minutes. The tests carried out are
measurements of the thickness and hardness of microvickers. The highest layer
thickness occurred in specimens with a current strength of 3 A and a time of 50
minutes of 2,522 μm. While the lowest value occurred in specimens with a strong
current of 2A and a time of 40 minutes of 1.6 μm. Then the highest micro hardness
value of 420,498 VHN, occurred in specimens with a strong current of 3A and a time
of 50 minutes. While the lowest value of 213,088 VHN, occurred in specimens with a
strong current of 2A and a time of 40 minutes.
Keywords : Coating, Electroplating Hard Chrome, Current, Time, Thickness,
Hardness, Steel, JIS G 3131 SPHC.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Coating, Electroplating Hard Chrome, Current, Time, Thickness, Hardness, Steel, JIS G 3131 SPHC.
Subjects:	T Technology > T Technology (General)
Divisions:	Faculty of Engineering, Science and Mathematics > School of Engineering Sciences
Depositing User:	Eko Yuli
Date Deposited:	04 Oct 2022 04:14
Last Modified:	04 Oct 2022 04:14
URI:	http://eprints.upnyk.ac.id/id/eprint/31239