ZUWANSAH SIAGIAN, ANGGA (2015) KAJIAN PENGARUH TOTAL MOISTURE BATUBARA TERHADAP KINERJA PULLVERIZER DI PT. SEMEN INDONESIA (PERSERO) TBK. PABRIK TUBAN I TUBAN, JAWA TIMUR. Other thesis, UPN ''VETERAN'' YOGYAKARTA.
Preview |
Text
RINGKASAN DAN ABSTRACT.pdf Download (238kB) | Preview |
Abstract
PT. Semen Indonesia (Persero) Tbk. pabrik Tuban I dalam memproduksi
semen memanfaatkan batubara sebagai bahan bakar pada proses pembakaran
dalam tanur putar. Sebelum dimanfaatkan, batubara terlebih dahulu dikecilkan
ukurannya dengan cara digiling ke dalam pullverizer, sehingga memperoleh
ukuran butir batubara -200 mesh. Hal ini bertujuan untuk dapat memperluas
bidang kontak antara batubara dengan udara, sehingga dalam proses pembakaran
tanur putar dapat lebih optimal.
Standar kapasitas pullverizer pada pabrik Tuban I sebesar 50 ton/jam
dengan efektifitas 100%, hasil kapasitas pullverizer yang dihasilkan dapat
dipengaruhui oleh kandungan kadar air umpan batubara yang digiling. Untuk
dapat mencapai kapasitas dan efektifitas pullverizer yang sesuai dengan standar
kapasitas pullverizer pabrik Tuban I, maka diperlukan penelitian pengaruh kadar
air umpan batubara terhadap hasil kapasitas dan efektifitas pullverizer yang
dihasilkan.
Permasalahan yang terjadi adalah kinerja pullverizer yang digunakan pada
pabrik Tuban I tidak sesuai dengan standar yang digunakan. Hal ini membuktikan
adanya penurunan dalam kinerja pullverizer yang dihasilkan, sehingga kapasitas
pullverizer pada bulan Februari 2014 pabrik Tuban I hanya dapat mencapai ratarata
41,58 ton/jam dengan efektifitas 83,16 %.
Berdasarkan hasil penelitian rendahnya kapasitas dan efektifitas pullverizer
pada pabrik Tuban I disebabkan tingginya kadar air total umpan batubara yang
digiling pullverizer, kadar air total umpan batubara pada bulan Februari 2014 rata
– rata sebesar 20,78 %. Oleh karena itu diperlukannya mengetahui berapa kadar
air total maksimum untuk sebagai umpan pullverizer, sehingga pullverizer dapat
sesuai dengan standar pabrik Tuban I sebesar kapasitas 50 ton/jam dengan
efektifitas 100%.
Untuk meningkatkan efektifitas hasil kinerja pullverizer hingga mencapai
50 ton/jam dengan efektifitas 100%, maka kadar air total untuk umpan pullverizer
pada pabrik Tuban I, harus memiliki kadar air total maksimum sebesar 15 %.
The Tuban I plant of PT. Semen Indonesia (Persero) Tbk in producing
cement utilizes coal as a fuel in the rotary kiln combustion process. Before being
utilized, the coal is first reduced in size by milling it into a pullverizer so as to
obtain 200-mesh sized coal grains. It aims to enlarge the contact area between the
coal and air in order to get the optimal rotary kiln combustion process.
The standard pullverizer capacity in Tuban I plant is 50 tons/hour with
100% effectiveness; the resulting pullverizer capacity may be influenced by the
moisture content of the coal feed. To achieve the capacity and effectiveness in
accordance with the standard of Tuban I plant, it is necessary to study the effect of
the coal feed moisture content on the pullverizer resulting capacity and
effectiveness.
The problem that occured was that performance of the pullverizer utilized
in Tuban I plant does not comply with the standard. It showed a decline in the
resulting performance that the pullverizer capacity of Tuban I plant in February
2014 only reached an average of 41,58 tons/hour with 83,16% effectiveness.
Based on the study results, the low capacity and effectiveness of the
pullverizer of Tuban I plant were due to the high total moisture content of coal
feed milled by the pullverizer: the average total moisture content of coal feed in
February 2014 was 20,78%. Therefore, it is necessary to figure out the maximum
total moisture content of feed for the pullverizer to work in accordance with the
standard of Tuban I plant with a capacity of 50 tons/hour and 100% effectiveness.
To improve the effectiveness of pullverizer performance to be up to 50
tons/hour with 100% effectiveness, the pullverizer feed in Tuban I plant should
have a maximum total moisture content of 15%.
| Item Type: | Thesis (Other) |
|---|---|
| Subjek: | T Technology > TN Mining engineering. Metallurgy |
| Divisions: | x. Faculty of Engineering, Science and Mathematics > School of Engineering Sciences |
| Depositing User: | Erny Azyanti |
| Date Deposited: | 07 Jun 2016 02:55 |
| Last Modified: | 07 Jun 2016 02:55 |
| URI: | http://eprints.upnyk.ac.id/id/eprint/3107 |
Actions (login required)
 |
View Item |